牌号 |
热处理制度 |
硬度 |
|
|
HB |
HRC |
||
|
9Cr18 |
800～920℃缓冷退火 |
≤255 |
- |
|
9Cr18Mo |
800～920℃缓冷退火 |
≤269 |
- |
|
9Cr18MoV |
800～920℃缓冷退火 |
≤269 |
- |
|
9Cr18 |
1070℃油冷/200～300℃油、空冷回火 |
- |
≥55 |
|
9Cr18Mo |
1070℃油冷/200～300℃油、空冷回火 |
- |
≥55 |
|
9Cr18MoV |
1070℃油冷/200～300℃油、空冷回火 |
- |
≥55 |
|
牌号 |
热处理制度 |
硬度 |
|
|
HB |
HRC |
||
|
9Cr18 |
退火或高温回火 |
172～185 |
- |
|
9Cr18 |
1000～1050℃油冷/200～300℃回火 |
- |
55～64 |
|
9Cr18MoV |
退火或高温回火/油、空冷 |
207～229 |
55～59 |
|
9Cr18MoV |
1050℃油冷/200℃回火空冷 |
- |
≥55 |
|
淬火 |
回火温度/℃ |
硬度HRC |
Ak/J |
应力为96IN弯曲疲劳次数 |
|
1050～1060℃淬火 |
100 |
60 |
2.4 |
6.3×106 |
|
150 |
60 |
2.98 |
8.4×106 |
|
|
200 |
59 |
3.14 |
4.5×106 |
|
淬火温度/℃ |
硬度/HRC |
||||
|
淬火后 |
-75℃×1h |
100℃回火 |
160℃回火 |
200℃回火 |
|
|
1000 |
59 |
- |
58 |
57 |
55 |
|
- |
59 |
59.5 |
59.5 |
59 |
57 |
|
1050 |
60 |
- |
60 |
59 |
57 |
|
- |
60 |
61.5 |
61 |
61 |
59 |
|
1100 |
60.5 |
- |
60 |
59.5 |
57 |
|
- |
60.5 |
62 |
62 |
62 |
60.5 |